PASSOS, Sheila P et al. The effect of carbamide peroxide bleaching agents on the microhardness of dental ceramics. Acta odontol. latinoam. [online]. 2010, vol.23, n.2, pp.79-83. ISSN 1852-4834.

This study examined the effect of 10% and 16% carbamide peroxide bleaching agents on the surface microhardness of micro-particulate feldspathic ceramics (VM7 and VM13, Vita Zahnfabrik). Forty specimens (8-mm diameter, 2-mm thickness) were divided into four groups (n=10): G1- VM7 + 10% Whiteness, G2- VM7 + 16% Whiteness, G3- VM13 + 10% and G4- VM13 + 16% Whiteness. The home-use bleaching agents were applied for 8 hours on 15 days, and the specimens were stored in distilled water at 37°C. The Vickers hardness number (HV) was determined for each specimen. Data were analyzed by the Wilcoxon and Mann- Whitney tests (p<0.05). The microhardness values before exposure were: g1- 433 (57); g2- 486 (22); g3- 509 (28); g4- 518 (24), and after exposure: G1- 349 (32); G2- 496 (95); G3- 519 (38); G4- 502 (81). G2 exhibited a higher and significant difference than G1 in VM7 groups, and the effect of bleaching concentration was shown to be significant by the Mann-Whitney test. And for VM13, both the Wilcoxon and Mann-Whitney tests showed no significant differences. When using 10% carbamide peroxide, the microhardness of VM7 ceramic was affected, and there were no effect on the microhardness between VM7 and VM13 ceramics when 16% carbamide peroxide was used.

Palabras clave : Ceramics; Hardness; Tooth-bleaching agent.