CAMILOTTI, Veridiana et al. Microleakage of a self-adhesive resin cement after post cementation. Acta odontol. latinoam. [online]. 2011, vol.24, n.1, pp.104-109. ISSN 1852-4834.

The aim of this study is to evaluate the microleakage a self-adhesive cement recently marketed Rely X U100 (3M ESPE). Thirty roots of bovine teeth with 14 mm long were restored with selfadhesive cement and Glassix fiber post DC3 (FGM). Roots were randomly divided into three groups (n=10) according to the technique of placement of the cementing agent: G1 - Centrix syringe; G2 - Lentulo drill and G3 - Manual technical. After cementation, provisional restorations were fabricated with composite resin (Opallis/FGM) without the use adhesive system. After they were finished, polished and thermo cycled by 1000 cycles, in water at temperature of 5oC and 55oC, 30 seconds in each bath. For microleakage test each group of roots was immersed in recipients with Rodhamine B dye solution buffered at 2%, during 24 hours. After this time, the samples were washed in tap water, sectioned and evaluation of dye leakage. The values of infiltration were obtained by the qualitative method (scoring) and statistical analysis using Kruskal-Wallis test and also by the quantitative method (Image Tool) and statistical analysis using ANOVA one way. For both tests, no significant difference between the techniques of placement of the self-adhesive cement. Based on these findings, micro-infiltration was present in all groups, and the placement technique did not influence the degree of micro-leakage, both for the qualitative analysis as to the quantitative.

Palabras clave : Dental cements; Tooth root; Dental leakage.