ORIGINAL ARTICLE

https://doi.org/10.1016/j.ram.2018.05.002

Silver nanoparticles from Justicia spicigera and their antimicrobial potentialities in the biocontrol of foodborne bacteria and phytopathogenic fungi

Nanopartículas de plata de Justicia spicigera y sus potencialidades antimicrobianas en el control biológico de bacterias transmitidas por alimentos y hongos fitopatógenos

 

Erick Bernardo-Mazariegos^a,c, Benjamín Valdez-Salas^b, Daniel González-Mendoza^a, Ali Abdelmoteleb^a,d, Olivia Tzintzun Camacho^a, Carlos Ceceña Duran^a, Federico Gutiérrez-Miceli^c

^a Instituto de Ciencias Agrícolas de la Universidad Autónoma de Baja California (ICA-UABC), Carretera a Delta s/n C.P. 21705, Ejido Nuevo León, Baja California, Mexico
^b Instituto de Ingeniería de la Universidad Autónoma de Baja California, Calle de la Normal s/n y Boulevard Benito Juárez, 21100 Mexicali, Baja California, Mexico
^c Instituto Tecnológico de Tuxtla Gutiérrez Carretera panamericana km 1080, Chiapas, Mexico ^d Faculty of Agriculture, Botany Department, Menoufia University, Shebin El-Kom, Egypt

Received 20 October 2017; accepted 2 May 2018
Available online 17 July 2018

*Corresponding author.

E-mail address: danielg@uabc.edu.mx (D. González-Mendoza).

 

---

ABSTRACT

In the present work, the biosynthesis of silver-nanoparticles (AgNP) was evaluated using the aqueous extract from Justicia spicigera. The obtained silver nanoparticles were characterized using UV–visible spectroscopic techniques, energy dispersive X-ray spectrometers (EDS), zeta potential and dynamic light scattering. The antimicrobial activity of biosynthesized AgNP was tested against foodborne bacteria (Bacillus cereus, Klebsiella pneumoniae and Enterobacter aerogenes) and phytopathogenic fungi (Colletotrichum sp., Fusarium solani, Alternaria alternata and Macrophomina phaseolina). The elemental profile of synthesized nanoparticles using J. spicigera shows higher counts at 3 keV due to silver, confirming the formation of silver nanoparticles. Scanning electron microscopy (SEM) analysis showed a particle size between 86 and 100 nm with spherical morphology. AgNP showed effective antibacterial and antifungal activity against the tested organisms principally with B. cereus, K. pneumoniae, E. aerogenes, A. alternata and M. phaseolina. Therefore, further studies are needed to confirm the potential of AgNP from J. spicigera in the control of indicator organisms under field conditions.

Keywords

Biosynthesis; Silver nanoparticles; Justicia spicigera; Antimicrobial activity

RESUMEN

En el presente trabajo se evaluó la biosíntesis de nanopartículas de plata (AgNP) en presencia de una sal de plata y extractos acuosos de Justicia spicigera. Las nanopartículas así obtenidas fueron caracterizadas mediante técnicas espectroscópicas UV-visibles, espectrómetros de rayos X de energía dispersiva (EDS), potencial zeta y dispersión de luz dinámica. La actividad antimicrobiana de las AgNP biosintetizadas se probó frente a diversas bacterias transmitidas por alimentos (Bacillus cereus, Klebsiella pneumoniae y Enterobacter aerogenes) y hongos fitopatógenos (Colletotrichum sp., Fusarium solani, Alternaria alternata y Macrophomina phaseolina). El perfil elemental de las nanopartículas sintetizadas utilizando el extracto de J. spicigera mostró valores altos a 3 keV, lo que confirma la formación de nanopartículas de plata. El análisis por microscopía electrónica de barrido (SEM) reveló un tamaño de partícula entre 86 y 100 nm, con morfología esférica. Las AgNP mostraron una actividad antibacteriana y antifúngica efectiva contra los organismos evaluados, principalmente contra B. cereus, K. pneumoniae, E. aerogenes, A. alternata y M. phaseolina. Se necesitan más estudios para confirmar el potencial de las AgNP derivadas de J. spicigera en el control de organismos indicadores en condiciones de campo.

Palabras clave

Biosíntesis; Nanopartículas de plata; Justicia spicigera; Actividad antimicrobiana

---

 

Introduction

Silver has been used as an antimicrobial agent for centuries; the recent resurgence of interest for this element particularly focuses on the increasing threat of antibiotic resistance caused by the abuse of antibiotics¹¹. However, there are some limitations in using Ag ions or Ag salts as antimicrobial agents. Probable reasons include bacterial resistance to silver¹⁸. Nevertheless, this type of limitation can be eliminated by using silver in nano form. In this sense, the silver nanoparticles (AgNP) may penetrate inside the cell causing damage by interacting with phosphorus and sulfur-containing compounds such as DNA and protein¹⁶. Currently, various chemical and physical methods are known for the preparation of silver and other metal nanoparticles. However, these methods are very costly and hazardous for the environment¹³. In this sense, green nanotechnology has great importance due to the elimination of harmful reagents and the effective synthesis of expected products in an economical manner. In recent years, the use of plants as source of bioactive compounds for the reduction of silver nanoparticles has been highlighted, because of its eco-friendly, economical protocol and for providing a single step technique for the biosynthesis of nanoparticles¹². The family Acanthaceae, is characteristic of tropical regions of the world and its widespread distribution includes ecosystems in Asia, Africa, and the Americas⁷. In Mexico, Justicia spi-cigera (common name, muicle or muitle) is a plant that has been used as a natural pigment source for dying fabrics and crafts¹⁷. Nowadays, J. spicigera has been the focus of scientific interest mainly because of its significant content of phenolic compounds that contribute to its antioxidant and antidiabetic activity making this plant an interesting alternative for possible biotechnological applications⁵. However, studies about the use of J. spicigera for the phytosynthesis of AgNP as a green chemistry method are scarce. In the present study, we report the easy synthesis of AgNP by an environmentally friendly procedure involving the in situ reduction of Ag by J. spicigera extracts and the evaluation of their antimicrobial activity against bacterial and fungal strains.

Material and methods

Biosynthesis of silver nanoparticles (AgNP) from Justicia spicigera

To prepare AgNP from J. spicigera, leaves of this plant were collected in Chiapas, Mexico. Leaves were cut into small pieces and dried using an electric oven for 10 h at 50 °C. Then 20 g of dried leaves of J. spicigera were mixed with 200 ml of deionized water and heated at 60°C for 30 min. About 50 ml of aqueous J. spicigera leaf extract were then centrifuged at 1792 g (Thermo Scientific Sorvall Legend Micro 17 with dual Row 24 x 1.5/2.0ml Rotor) for 25 min to remove particulate matter and to obtain clear solutions which were then refrigerated to 4 °C for further use. For AgNP synthesis 10 ml of aqueous J. spicigera leaf extract were added into 40 ml of aqueous solution of 10 mM silver nitrate and heated to 60°C for 15min. Finally, a brown solution was formed, which stands as a preliminary identification of the formation of AgNP³. The AgNP were purified by centrifugation at 11 200 x g (Thermo Scientific Sorvall Legend Micro 17 with dual Row 24 x 1.5/2.0ml Rotor) for 15 min and the precipitate was thoroughly washed with sterile distilled water to get rid of any unwanted impurities and transferred to a freeze dryer. The obtained powder was used in antimicrobial assays.

Characterization of AgNP

To determine the bioreduction of silver ions and the production of AgNP, the absorption spectra of the solutions, J. spicigera: silver nitrate, were scanned in UV-visible (vis) spectra, between wavelengths of 350-500 nm in a spectrophotometer (DR6000^TM UV VIS Spectrophotometer, USA), having a resolution of 1 nm and using double distilled water as a blank reference.

Scanning electron microscopy (SEM) and energy dispersive X-ray (EDS)

The presence of AgNP from J. spicigera was confirmed by EDS, and the surface characterization was performed by the SEM analysis (JEOL 6010L; JEOL, Tokyo, Japan) with an accelerating voltage of 10 kV and a STEM support according to Arrieta et al.⁴.

Zeta potential and dynamic light scattering (DLS)

The hydrodynamic sizes and the zeta potential of biosynthesized AgNP in solution were analyzed using a Nanotrac Wave Instrument (Microtrac). Three milliliters of sample were transferred into the clear disposable zeta cell for zeta potential measurement. Measurements were made by dynamic light scattering (DLS) in the range of 0.1-1000 µm at 25 °C, using a laser wavelength of 780 nm and a scattering angle of 90°. DLS data were analyzed by the Microtrac FLEX operating software²⁷.

Antibacterial activity of AgNP

The effect of antibacterial activity of biosynthesized AgNP was determined using the disk diffusion method. Three types of bacteria, Bacillus cereus, Klebsiella pneumoniae, and Enterobacter aerogenes were tested. Bacteria cultures were grown in nutritious broth medium at 37 °C. After 24 h of growth, each microorganism was inoculated on the surface of nutrient agar plates at a concentration of 10⁵ cells/ml. Subsequently, sterile paper disks (6 mm in diameter) were placed on the surface of each inoculated plate. The plates were divided into two groups; in the first group, 30 µl of leaf extract and sterile distilled water were applied to the disks as positive and negative control, respectively. In the second group, sterile paper disks were placed on the agar plates, and 30 µl of 100mg/ml (w/v) samples were applied to the disks. All the plates were incubated at 32 °C for 24 h. After this period, the zone of inhibition which appeared as a clear area around the disks could be observed.

Effect of AgNP against phytopathogenic fungi

Antifungal activity of AgNP was performed by the dual culture technique in individual culture plates. The plates were divided into two quadrants; the first quadrant was prepared with 15 ml of PDA-AgNP (100mg/ml) and the second quadrants were only prepared with PDA medium. After an agar disk (6 mm) was taken from 4-day-old PDA culture plates of each fungus (Colletotrichum sp., Fusarium solani,

Alternaria alternate and Macrophomina phaseolina) and placed at the periphery of the PDA-AgNP plates. Another agar disk of the same size of each fungus was also placed at the periphery but on the opposing end of the same Petri dish (PDA + J. spicigera extract). The plates were incubated at 27°C for 9 days and the zone of inhibition was recorded.

Statistical analysis

Differences between the treatments were evaluated using one-way analyses of variance and the Tukey's test (p < 0.05), and SAS Version 9.0 (SAS Institute, 2002) was used.

Results

Biosynthesis of AgNP-Justicia spicigera

The UV-visible spectroscopy is an important preliminary technique to ascertain the formation and stability of metal nanoparticles in aqueous suspension. Thus, the formation of AgNP by reduction of aqueous Ag+ during exposure to the aqueous extract of J. spicigera was followed and characterized by UV-visible spectroscopy.

As shown in Figure 1, the surface plasmon resonance of the AgNP was centered at approximately 487nm.

Figure 1. UV–vis absorption spectrum of silver nanoparticles from J. spicigera extract.

Zeta potential and dynamic light scattering (DLS)

The average hydrodynamic size and zeta potential of the AgNP was determined by DLS as shown in Figure 2. The sample was a mixture of AgNP of different sizes; DLS intensity analysis gave two broad peaks and was weighted toward the larger particles (z-average size of 4.04µm and 192 nm). These results suggest that DLS measurement may not be accurate for polydisperse samples due to its nature to respond toward larger particles. In addition, the zeta potential was found to be 0.2 mV for synthesized AgNP indicating less stability and thus, a tendency to agglomerate and form large particles.

Figure 2. Particle size distribution of silver nanoparticles from dynamic light scattering measurements.

Antimicrobial activity of synthesized silver nanoparticles

To investigate the antibacterial activity of the synthesized AgNP from J. spicigera against B. cereus, K. pneumoniae, and E. aerogenes, the concentration of AgNP (100mg/ml) was used. Our results showed that the antibacterial activity of disks prepared with AgNP (100mg/ml) doses was more effective in comparison with the impregnated disk with control (J. spicigera leaf extract) (Table 1).

Table 1 Inhibition of different bacteria by AgNP from Justicia spicigera

Antifungal activity of synthesized silver nanoparticles

The inhibition effect of AgNP from J. spicigera was examined in PDA. A significantly higher mycelial growth inhibition (p <0.05) was observed on PDA-AgNP medium against M. phaseolina and A. alternate with 79.77% and 60.10% of radial growth inhibition, respectively, when compared to the control after nine days of incubation (Table 2 and Fig. 4). However, in Colletotrichum sp., and F. solani a lower mycelial growth inhibition (40% and 35%, respectively) was observed after nine days of incubation.

Table 2 Mycelial growth inhibition by AgNP from Justicia spicigera

Discussion

SEM and EDS analysis

EDS analysis gives qualitative as well as quantitative status of elements that may be involved in the realization of nanoparticles⁹. In this sense, the elemental profile of synthesized nanoparticles using J. spicigera shows higher counts at 3keV due to silver, confirming the formation of silver nanoparticles (Fig. 3A). The elemental profile also showed the presence of oxygen (11.41%), carbon (64.35%) and chlorine (6.10%) respectively (Fig. 3). On the other hand, the SEM provided further insight into the morphology and size details of the silver nanoparticles. In the present study the SEM analysis showed a particle size between 86 and 100 nm with spherical morphology (Fig. 3B).

Figure 3 EDS (A) and SEM (B) image of silver nanoparticles produced from J. spicigera.

Figure 4 Antifungal activity of J. spicigera extract and AgNP from J. spicigera against A. alternate (a), Colletotrichum sp. (b), M. phaseolina (c) and F. solani (d).

Nowadays, synthesizing metal nanoparticles using plants has been extensively studied and has been recognized as a green and efficient way for further exploiting plants as convenient nanofactories^21,23. In this study the biosynthesis of silver nanoparticles from J. spicigera showed a reddish brown color in the aqueous solution as a result of a bioreduction mechanism of metal nanoparticles by secondary metabolites (for e.g., phenolic acid, flavonoids and alkaloids) present in the aqueous extract of J. spicigera. Similarly, Abdelmoteleb et al.² and Pulit-Procial et al.^19,20 reported that the silver nanoparticles from Pluchea sericea exhibited striking colors, from light yellow to brown in the aqueous solution due to the increasing number of AgNP formed as a result of the reduction of Ag ions by secondary metabolites present in the aqueous solution. Therefore, the secondary metabolites such as flavonoids and phenols present in the aqueous extract of J. spicigera may be responsible for stabilizing the synthesized nanoparticles; however, the probable mechanism is unclear and further investigation are required. In this sense, Sahadevan et al.²² reported that flavonoids present in leaf extract are responsible for reducing silver ions and capping for Ag-nanoparticles. On the other hand, the interaction, AgNP and extract of J. spicigera by DLS analyses showed a major particle size distribution peak at 4.04 µm and a second peak at 192 nm, which represented the existence of interaction between Ag ions and biomolecules from J. spicigera, which resulted in their further aggregation. This result is consistent with that previously reported by Yu et al.²⁶ who found that the formation of new peaks of enlarged sizes indicated the aggregations of different components after mixing the silver solution with apple extract.

As expected, the SEM measured size (89 nm) is considerably shorter than the DLS size. According to Erjaee et al.⁸, these differences possibly reflect the fact that SEM only measures a number-based size distribution of the physical size while DLS measures the hydrodynamic diameter of the particle, plus biomolecules that are attached to the surface of AgNP in the solution. On other hand, Kumari et al.¹⁴ found that the DLS mean from AgNP of Cordia dichotoma was approximately 80% (90.42 nm) higher than the TEM mean size of 10 nm. In this sense, it is important to consider that the enlargement of size distributions induces errors to DLS particle sizing measurements when compared to the TEM analyses. Moreover, it is known, that metallic Ag-nanocrystals show a typical optical absorption peak at 2.9 to 3.2 keV due to their surface plasmon resonance⁸. In this context, in the present study the elemental analysis of AgNP reveals the highest proportion of silver (Ag) followed by peaks carbon and oxygen atoms that suggested the presence of organic molecules on the surface of silver nanoparticles, which might have come from the plant leaf extract. In our study, the antibacterial activity of AgNP from J. spicigera is not completely clear; however, recent studies mention that bactericidal efficiency could be the result of an electric charge on the surface of AgNP, oxidative stress induction, metal ion release, or non-oxidative mechanisms that can occur simultaneously¹. Additionally, certain studies have proposed that AgNP prompt neutralization of the surface electric charge of the bacterial membrane and change its penetrability, ultimately leading to bacterial death²⁵. Bose and Chatterjee⁶ also found that AgNP from Justicia adhatoda, significantly increase cell permeability and affect proper transport through the plasma membrane. Therefore, further studies are needed to confirm the potential of AgNP from J. spicigera in the biocontrol of the evaluated bacteria. Silver nanoparticles from different sources have a biotechnological potential against fungi due to alterations and structural changes in hyphae, cell wall and germination, caused by the applications of nanoparticles¹⁰. However, in the current study, this effect in Colletotrichum sp., and F. solani was not registered. In this sense, the AgNP tolerance observed in Colletotrichum sp., and F. solani can be attributed to their complex multicellular organization¹⁵. In this sense, authors such as Harris⁹ and Villamizar-Gallardo et al.²⁴ explain that this tolerance can be attributed to the fact that F. solani produces macroconidia which, by presenting complex cellular organization, probably hinders the internal transport of AgNP, thus decreasing their fungicidal effect.

Conclusions

In the present study the bioreduction of silver nitrate solution using J. spicigera leaves extract offers environmental friendly and simple method for green synthesis of silver nanoparticles. These nanoparticles showed effective antibacterial and antifungal activity against B. cereus, K. pneumoniae, E. aerogenes, A. alternata and M. phase-olina. Future studies are required for evaluating the effect of application of these nanoparticles under field conditions.

Conflict of interest

The authors declare that they have no conflicts of interest.

Acknowledgements

The authors are particularly gratefully to Conacyt (219750), SEFOA and Tecnológico Nacional de México.

References

1. Abbas A, Ghahramani Y, Gholami A, Hemmateenejad B, Dorostkar S, Nabavizadeh M, Shargui H. The effect of charge at the surface of silver nanoparticles on antimicrobial activity against gram-positive and gram-negative bacteria: a preliminary study. J Nanomater. 2015, http://dx.doi.org/10.1155/2015/720654.         [ Links ]

2. Abdelmoteleb A, Valdez-Salas B, Carrillo-Beltran M, Duran-Hernandez D, Gonzalez-Mendoza D. Green synthesis of silver nanoparticles using Pluchea sericea a native plants from Baja California Mexico and their potential application as antimicrobials. Iran J Sci Technol A. 2016, http://dx.doi.org/10.1007/s40995-016-0019-6.         [ Links ]

3. Ahmed S, Saifullah M, Babu LS, Ikram S. Green synthesis of silver nanoparticles using Azadiracht indica aqueous leaf extract. J Radiat Res Appl Sci. 2016;9:1-7.         [ Links ]

4. Arrieta EC, Valdez B, Carrillo M, Curiel MA, David-Mateos F, Arturo-Ramos R, Rosas N, Maria-Bastidas J. Silver nanoparticles biosynthesized by secondary metabolites from Moringa oleifera stem and their antimicrobial properties. Afr J Bio-technol. 2017;16:400-7.         [ Links ]

5. Baqueiro-Pena I, Guerrero-Beltrán JA. Physicochemical and antioxidant characterization of Justicia spicigera. Food Chem. 2017;218:305-12.         [ Links ]

6. Bose D, Chatterjee S. Antibacterial activity of green synthesized silver nanoparticles using Vasaka (Justicia adhatoda L.) leaf extract. Indian J Microbiol. 2015;55:163-7.         [ Links ]

7. Correa G, Alcantara A. Chemical constituents and biological activities of species of Justicia: a review. Rev Bras Farmacogn. 2012;22:220-38.         [ Links ]

8. Erjaee H, Rajaian H, Nazifi S. Synthesis and characterization of novel silver nanoparticles using Chamaemelum nobile extract for antibacterial application. Adv Nat Sci-Nanosci. 2017;8:025004.         [ Links ]

9. Gowramma B, Keerthi U, Rafi M, Muralidhara Rao D. Biogenic silver nanoparticles production and characterization from native strain of Corynebacterium species and its antimicrobial activity. 3 Biotech. 2015;5:195-201.         [ Links ]

10. Harris SD. Morphogenesis in germinating Fusarium graminearum macroconidia. Mycologia. 2005;97:880-7.         [ Links ]

11. Huh AJ, Kwon YJ. Nanoantibiotic: a new paradigm for treating infectious diseases using nanomaterials in the antibiotics resistant era. J Control Release. 2011;156: 128-45.         [ Links ]

12. Ibrahim HMM. Green synthesis and characterization of silver nanoparticles using banana peel extract and their antimicrobial activity against representative microorganisms. J Radiat Res Appl Sci. 2015;8:265-75.         [ Links ]

13. Jeong SH, Yeo SY, Yi SC. The effect of filler particle size on the antibacterial properties of compounded polymer/silver fibers. J Mater Sci. 2005;40:5407-11.         [ Links ]

14. Kumari RM, Thapa N, Gupta N, Kumar A, Nimesh S. Antibacterial and photocatalytic degradation efficacy of silver nanoparticles biosynthesized using Cordia dichotoma leaf extract. Adv Nat Sci-Nanosci. 2016;7:045009.         [ Links ]

15. Lamsal K, Kim SW, Jung JH, Kim YS, Kim KS, Lee YS. Application of silver nanoparticles for the control of Colletotrichum species in vitro and pepper anthracnose disease in field. Mycobiology. 2011;39:194-9.         [ Links ]

16. Nanda A, Saravanan M. Biosynthesis of silver nanoparticles from Staphylococcus aureus and its antimicrobial activity against MRSA and MRSE. Nanomedicine. 2009;5:452-6.         [ Links ]

17. Pavón-García LM, Pérez-Alonso C, Orozco-Villafuerte M, Pimentel-Gonzalez DJ, Rodriguez-Huezo ME, Vernon-Carter EJ. Storage stability of the natural colorant from Justicia spicigera microencapsulated in protective colloids blends by spray-drying. Int J Food Sci Technol. 2011;6: 1428-37.         [ Links ]

18. Percival SL, Bowler PG, Russell D. Bacterial resistance to silver in wound care. J Hosp Infect. 2005;60:1-7.         [ Links ]

19. Pulit-Prociak J, Banach M. The use of plant materials in the process of obtaining silver and gold nanoparticles. J Comput Theor Nanosci. 2016;13:2697-704.         [ Links ]

20. Pulit-Prociak J, Stoktosa K, Banach M. Nanosilver products and toxicity. Environ Chem Lett. 2015;13:59-68.         [ Links ]

21. Rai A, Singh A, Ahmad A, Sastry M. Role of halide ions and temperature on the morphology of biologically synthesized gold nanotriangles. Langmuir. 2006;22: 736-41.         [ Links ]

22. Sahadevan R, Sivakumar P, Karthika P, Sivakumar-Muralidharan NG, Devendran P. Biosynthesis of silver nanoparticles from active compounds Quacetin-3-O-B-D-galactopyranoside containing plant extract and its antifungal application. Asian J Pharm Clin Res. 2013;6:76-9.         [ Links ]

23. Singh P, Kim YJ, Zhang D, Yang DC. Biological synthesis of nanoparticles from plants and microorganisms. Trends Biotechnol. 2016;34:588-99.         [ Links ]

24. Villamizar-Gallardo R, Osma Cruz JF, Ortiz-Rodriguez O. Fungicidal effect of silver nanoparticles on toxigenic fungi in cocoa. Pesq Agropec Bras. 2016;12:1929-36.         [ Links ]

25. Wang L, Hu C, Shao L. The antimicrobial activity of nanoparticles: present situation and prospects for the future. Int J Nanomedicine. 2017;12:1227-49.         [ Links ]

26. Yu Q, Li J, Zhang Y.Wang Y.Liu L, Li M. Inhibition of gold nanoparticles (AuNPs) on pathogenic biofilm formation and invasion to host cells. Sci Rep. 2016;6: 26667.         [ Links ]

27. Zhou C, Qi W, Lewis EN, Carpenter JF. Concomitant Raman spectroscopy and dynamic light scattering for characterization of therapeutic proteins at high concentrations. Anal Biochem. 2015;472:7-20.         [ Links ]